Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited.
Ozellikleri
- Intended for build-up before final overlay, and as a final surface for metal-to-metal wear with moderate impact
- 自动和semiautomatic operation on mild and low alloy steels
- Good resistance to cross checking
Tipik Uygulamalar
- For Build-Up: Tractor rollers, Trunnions, Idlers and Crane wheels
- For Hardfacing: Shafts, Track rails and Idlers
Kaynaklama Konumları
- Flat/Horizontal and circumferential
Servis Bilgileri
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER.SDS Arama sayfası
Test sonucunu görünsorumluluk reddi
MECHANICAL PROPERTIES
| Flux | Classification | Number of layer | Hardness Rockwell C |
|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 6 | 27 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Mn | %Mo | %Si |
|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.11 | 2.5 | 0.5 | 0.4 |
| Lincolnweld® 801® | Typical Result | 0.11 | 2.5 | 0.5 | 0.4 |
| Lincolnweld® 801® | Typical Result | 0.11 | 2.7 | 0.5 | 0.6 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity | Wire Feed Speed m/min (in/min) |
Voltage volts |
Approx. Current amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.5 (60) | 26 | 220 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 27 | 360 |
| 3/32 in (2.4 mm) | DC+ | 4.6 (180) | 28 | 500 |
| 1/8 in (3.2 mm) | DC+ | 1.3 (50) | 27 | 310 |
| 1/8 in (3.2 mm) | DC+ | 2.0 (80) | 28 | 450 |
| 1/8 in (3.2 mm) | DC+ | 2.8 (110) | 28 | 600 |