DETAILS
Ideal for building up on carbon and low alloy steels. Use as an underbase for carbon steel parts prior to hardfacing. Great compressive strength under heavy loading. Deposits are generally crack free, machinable and can be flame cut. Deposit thickness is unlimited. Used in Metal-to-Metal wear applications, works best in non-lubricated rolling or sliding.
Features
- Use on carbon, and low alloy steels
- Deposit is unlimited layers
- Metal-cored wire that is most widely used for caster roll rebuilding
- Works well with Lincolweld 801 or 802 Flux
Disclaimers
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER.SDS Search page
See test resultdisclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 46-50 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Si |
|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.20 | 12.0 | 1.2 | 0.5 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity | Wire Feed Speed m/min (in/min) |
Voltage volts |
Approx. Current amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 250 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 375 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 450 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 350 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 500 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 625 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 475 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 650 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 800 |